Method of scrapping furnace bottom section of blast furnace

ABSTRACT

A solidified residual iron within a blast furnace is suspended up by employing a shell suspending device fixed to a tuyere arranged in a lower end portion of an upper portion of a furnace body suspended by a lift jack and a solidified residual iron suspending band, thereafter is descended by employing the lift jack and is mounted on a horizontally moving table. Subsequently, the horizontally moving table mounting the solidified residual iron thereon is moved onto a furnace outer truck rail from a furnace inner truck rail so as to be taken out of the furnace by operating a center hole jack arranged near the furnace outer truck rail, whereby an operation of taking out the solidified residual iron within the blast furnace out of the furnace is economically performed for a short time.

1. FIELD OF THE INVENTION

[0001] The present invention relates to a method of scrapping a furnace bottom section of a blast furnace, and more particularly to a method of scrapping a furnace bottom section of a blast furnace which can convey a solidified residual iron left in the furnace bottom section after performing a blowing-down for revamping the blast furnace out of the furnace.

2. PRIOR ART

[0002] When operating the blast furnace for a long time, a lining brick is significantly corroded. When leaving the corrosion, in an upper portion of the blast furnace, a crack is generated in a shell provided on an outer periphery as a pressure container and a gas or the like is injected out, and in a lower portion of the blast furnace, a carbon brick in the furnace bottom section is corroded and a dissolved material melts down the shell and flows out. In this case, there is a case that a water vapor explosion is generated by a stave cooling water or a shell cooling water. Accordingly, the blast furnace is blown out and an inner portion thereof is revamped once per ten and some years.

[0003] At a time of revamping the blast furnace, an opening portion is formed at first by partly breaking the shell in the furnace bottom section of the blast furnace and the lining brick by means of a construction machinery such as a back hoe, a shovel or the like, and the construction machinery is introduced into the inner portion of the furnace bottom section. Then, a coke left in the furnace bottom section is pressed out of the furnace by the construction machinery so as to be removed. Thereafter, it is necessary that an operator enters within the furnace and crushes the solidified residual iron left in a lower portion thereof, the solidified residual iron mainly containing a pig iron with which a slag or a coke is mixed, by employing a rock drill or a blasting, so as to convey the solidified residual iron out of the furnace.

[0004] The solidified residual iron is firmly integrated and hard to be decomposed as is different from a collapsible solidified material, and is divided in accordance with a blast. It has been necessary to at first form a multiplicity of bores in the solidified residual iron by a boring drill or an oxygen lance prior to the blast and charge a dynamite therein, prior to the blast. In this boring, blasting and dividing method mentioned above, since a long time is required for the boring operation, a long period is required for the construction, so that the blasting operation avoids the other scrapping operations. Further, since the crushed materials are dispersed at a time of explosion and a significant danger and loud sound are generated, the operation performed in the periphery of the blast furnace is necessarily interrupted at a time of blasting.

[0005] In this case, since a period of the construction for revamping the blast furnace is required to be reduced as much as possible, the scrapping operation is started before the lining brick and the solidified residual iron within the furnace body are cooled to a room temperature. Accordingly, an environment of the operation is a bad environment in which a temperature is high and a lot of dusts are generated. Further, since the lining brick and the solidified residual iron are hard and heavy, it is necessary to divide them into small components in order to convey out from the opening portion provided in the furnace bottom section. For the reasons mentioned above, the time required for the conventional scrapping operation has become very long and as a result, a lot of cost for operation has been required.

[0006] Further, an outrigger crane placed in a supporting column for maintenance may be used. In this case, the shell in the furnace bottom section of the blast furnace has been cut so as to form short strips having a weight of 5 to 50 tons and has been taken out by the outrigger crane, and the solidified residual iron is removed out of the furnace from the opening portion provided in the furnace bottom section of the blast furnace.

[0007] Further, as another method, a method of revamping an inner portion of a blast furnace is disclosed in Japanese Unexamined Patent Publication Nos. 10-96005 and 7-197112. A method of scrapping a furnace bottom section of a blast furnace described in Japanese Patent Unexamined Publication No. 10-96005 is structured such as to cut a lower portion of the furnace, suspend and fixe a furnace body of the blast furnace by a supporting column, thereafter scrap a shell in the lower portion of the furnace, horizontally cut a solidified residual iron within the blast furnace by a wire saw and integrally take out the solidified residual iron. On the contrary, a method of conveying a solidified residual iron in a furnace bottom section of a blast furnace out of the furnace described in Japanese Patent Unexamined Publication No. 7-197112 is structured such as to place a jack between a solidified residual iron in the periphery within the blast furnace and a furnace bottom section brick so as to lift up in a vertical direction, thereafter insert an object for reducing a coefficient of friction such as a cylinder or the like and take out the solidified residual iron.

[0008] However, the conventional methods of scrapping the furnace bottom section of the blast furnace have the following problems.

[0009] (1) In the method using the outrigger crane, since the solidified residual iron within the blast furnace is a large-size solidified residual iron having a weight of about 500 ton while the suspending capacity of the outrigger crane is about 70 to 200 ton, it is necessary to divide the solidified residual iron into small pieces.

[0010] (2) In the method described in Japanese Patent Unexamined Publication No. 10-96005, a long time is required for the cutting operation of the brick and a lot of labors are required for taking out the solidified residual iron.

[0011] (3) In the method described in Japanese Patent Unexamined Publication No. 7-197112, a size of the conveyed-out solidified residual iron is limited even when the coefficient of friction of the solidified residual iron and the furnace bottom section brick is reduced by using the cylinder or the like.

[0012] Further, since the supporting column for supporting the furnace body is provided in the outer periphery of the blast furnace, it is necessary to perform the operation so as not to interfere with the supporting column at a time of conveying the solidified residual iron out of the furnace whichever method is employed.

[0013] The present invention is made by taking the above matters into consideration, and an object of the present invention is to provide a method of scrapping a furnace bottom section at a time of revamping a blast furnace which can effectively discharge a solidified residual iron left in the furnace bottom section for a short time.

SUMMARY OF THE INVENTION

[0014] In accordance with the present invention, there is provided a method of scrapping a furnace bottom section of a blast furnace comprising the steps of:

[0015] horizontally cutting a furnace body of the blast furnace after being blown out at a position higher than a solidified residual iron left in the furnace bottom section;

[0016] suspending an upper furnace body above the cutting position by employing vertically moving means placed in a supporting column;

[0017] taking out at least a part of a shell and a lining brick in a lower furnace body below the cutting position all around the periphery; and

[0018] thereafter conveying the solidified residual iron out of the furnace,

[0019] wherein the upper furnace body and the solidified residual iron are integrally connected by using a suspending device before conveying the solidified residual iron out of the furnace, and the upper furnace body and the solidified residual iron are vertically moved by using the vertically moving means.

[0020] In accordance with the invention mentioned above, it is preferable to make the structure such that a plurality of cavities are provided along a peripheral portion of the solidified residual iron and at a plurality of portions between the solidified residual iron and the furnace bottom brick before conveying the solidified residual iron out of the furnace, the solidified residual iron is jacked up by a lifting-up jack arranged in the cavity so as to form a gap between the solidified residual iron and the furnace bottom brick, a solidified residual iron suspending band (herein after referred to as suspending band) is inserted into the gap, thereafter the upper furnace body suspended in the supporting column is descended by using the vertically moving means so that the suspending band is connected to the suspending device fixed to a lower portion of the upper furnace body, next the upper furnace body is suspended up together with the solidified residual iron by using the vertically moving means so that an operating space is formed between the solidified residual iron and the furnace bottom brick or a bottom plate of the blast furnace, a horizontally moving table is moved on the furnace bottom brick or the bottom plate of the blast furnace, thereafter the upper furnace body and the solidified residual iron are descended by using the vertically moving means so as to be mounted on the horizontally moving table, next the suspending device fixed to the lower portion of the upper furnace body is separated, thereafter the upper furnace body is evacuated upward by using the vertically moving apparatus, and the horizontally moving table mounting the solidified residual iron thereon is moved from the inner portion of the furnace to the outer portion of the furnace.

[0021] Further, it is preferable to make the structure such that the suspending device is fixed to a tuyere of the upper furnace body.

[0022] Further, it is preferable to make the structure such that a surface layer portion of the furnace bottom brick is flattened under the operating space formed between the solidified residual iron and the furnace bottom brick, or the furnace bottom brick is removed, thereafter a furnace inner rail is placed on the furnace bottom brick or the bottom plate of the blast furnace, and the horizontally moving table is moved on the furnace inner rail.

[0023] Further, it is preferable to make the structure such that a surface layer portion of the furnace bottom brick is flattened under the operating space formed between the solidified residual iron and the furnace bottom brick, or the furnace bottom brick is removed, thereafter the horizontally moving table having a solidified residual iron receiving table detachably arranged in a plurality of through holes is moved onto the furnace brick or the bottom plate of the blast furnace, the upper furnace body and the solidified residual iron are descended by using the vertically moving means so as to be mounted on the solidified residual iron receiving table, a lower end surface of the solidified residual iron receiving table is grounded on the furnace bottom brick or the bottom plate of the blast furnace due to a deadweight of the solidified residual iron so that a construction space is formed between the horizontally moving table and the furnace bottom brick or the bottom plate of the blast furnace, the furnace inner rail is placed on the furnace bottom brick or the bottom plate of the blast furnace under the construction space, thereafter the upper furnace body and the solidified residual iron are suspended up by using the vertically moving means so that the solidified residual iron receiving table is taken out from the horizontally moving table, the upper furnace body and the solidified residual iron are descended by using the vertically moving means so as to be mounted on the horizontally moving table, next the suspending device fixed to the lower end portion of the upper furnace body is separated, thereafter the upper furnace body is evacuated upward by using the vertically moving apparatus, and the horizontally moving table mounting the solidified residual iron thereon is moved to the outer portion of the furnace from the inner portion of the furnace.

[0024] Further, it is preferable to make the structure such that a receiving shelf is provided in the through hole provided in the horizontally moving table, the solidified residual iron receiving table is supported to the receiving shelf via a plurality of springs by a bracket provided on an upper side surface thereof, a lower end surface of the solidified residual iron receiving table is moved apart from the furnace bottom brick or the bottom plate of the blast furnace due to an elastic force of the spring when the horizontally moving table is moved onto the furnace bottom brick or the bottom plate of the blast furnace, the spring is compressed via the bracket when the solidified residual iron is mounted on the solidified residual iron receiving table so that the lower end surface of the solidified residual iron receiving table is grounded on the furnace bottom brick or the bottom plate of the blast furnace, and the construction space is formed between the horizontally moving table and the furnace bottom brick or the bottom plate of the blast furnace.

[0025] Further, it is preferable to make the structure such that the horizontally moving table arranged on the furnace inner rail is moved via a roller or a slide shoe arranged in a lower portion of the horizontally moving table.

[0026] Further, it is preferable to make the structure such that the slide shoe is arranged within a groove formed in the furnace inner rail, a friction coefficient reducing member is interposed between the slide shoe and the groove formed in the furnace inner rail, and the horizontally moving table is moved due to a slide motion along the groove formed in the furnace inner rail of the slide shoe.

[0027] Further, it is preferable to make the structure such that the friction coefficient reducing member is made of a Teflon and/or a stainless steel.

[0028] Further, it is preferable to make the structure such that a shape of the suspending band is formed in a Y shape.

[0029] Further, it is preferable to make the structure such that a shape of the suspending band is formed in a web shape, and the solidified residual iron is suspended up by crossing two web-like suspending bands so as to form an X shape.

[0030] Further, it is preferable to make the structure such that the solidified residual iron is separated so as to be suspended up together with the upper furnace body by using the vertically moving means.

[0031] Further, it is preferable to make the structure such that the solidified residual iron mounted on the horizontally moving table is separated.

[0032] Further, it is preferable to make the structure such that a beam is arranged within the upper furnace body, the beam and the solidified residual iron are connected by using the suspending-up member, and the solidified residual iron is suspended up by using the suspending-up member and the suspending band.

BRIEF DESCRIPTION OF THE DRAWINGS

[0033]FIG. 1 is a front elevational view of a blast furnace;

[0034]FIG. 2 is a front elevational view showing a state of a furnace bottom section when taking out a shell in the furnace bottom section;

[0035]FIG. 3 is a front elevational view showing a state of a collapsible solidified material and a solidified residual iron when taking out the shell in the furnace bottom section;

[0036]FIG. 4 is a plan view showing a state of arranging a lifting-up jack in a cavity in the periphery of the solidified residual iron;

[0037]FIG. 5 is a cross sectional view showing a state of jacking up the solidified residual iron by the lifting-up jack;

[0038]FIG. 6A is a cross sectional view showing a state in which a suspending band is inserted between the solidified residual iron lifted up by the lifting-up jack and a furnace bottom brick;

[0039]FIG. 6B is a partly enlarged cross sectional view showing a state in which a suspending device is attached to a tuyere;

[0040]FIG. 7 is a front elevational view showing a state in which the suspended upper furnace body is descended and the suspending band is connected to the suspending device fixed to the tuyere;

[0041]FIG. 8 is a front elevational view showing a state in which the upper furnace body is ascended by a lift jack, the solidified residual iron is suspended up by using the suspending device and the suspending band and an operating space is formed above the furnace bottom brick;

[0042]FIG. 9 is a front elevational view showing a state in which a surface layer portion of the furnace bottom brick is flattened by a construction machinery;

[0043]FIG. 10 is a cross sectional view showing a state after the surface layer portion of the furnace bottom brick is flattened;

[0044]FIG. 11 is a cross sectional view showing a state in which a furnace inner rail is placed on a surface of the furnace bottom brick;

[0045]FIG. 12 is a front elevational view showing a state in which a horizontally moving table is moved onto the furnace inner rail;

[0046]FIG. 13 is a side elevational view showing a state in which a roller structure body provided in a lower portion of the horizontally moving table is arranged in correspondence to a groove type furnace inner rail;

[0047]FIG. 14 is a side elevational view showing a state in which a roller structure body constituted by a guide roller and a moving roller provided in the lower portion of the horizontally moving table is arranged in correspondence to the groove type furnace inner rail;

[0048]FIG. 15 is a front elevational view showing a multiplicity of moving rollers connected by an endless chain;

[0049]FIG. 16 is a side elevational view showing a state in which a slide shoe arranged on a lower surface of the horizontally moving table is arranged in correspondence to the groove type rail;

[0050]FIG. 17 is a side elevational view showing an I-type rail placed on the furnace bottom brick;

[0051]FIG. 18 is a front elevational view showing a state in which the upper furnace body is descended by a lift jack and the solidified residual iron supported via the suspending band is mounted on the horizontally moving table;

[0052]FIG. 19 is a front elevational view showing a state in which the upper furnace body is evacuated by being ascended by the lift jack and the horizontally moving table mounting the solidified residual iron thereon is moved to a furnace body transferring truck;

[0053]FIG. 20 is a front elevational view showing a state in which the horizontally moving table mounting the solidified residual iron thereon is moved onto a rack rail by operating a cylinder for moving arranged near the rack rail;

[0054]FIG. 21 is a front elevational view showing a state in which the horizontally moving table mounting the solidified residual iron thereon is mounted on an accumulating level adjusting structure of the furnace body transferring truck;

[0055]FIG. 22 is a front elevational view showing a state in which the furnace body transferring truck supporting the horizontally moving table having the solidified residual iron receiving table thereon waits near the furnace bottom section of a blast furnace;

[0056]FIG. 23 is a front elevational view showing a state in which the horizontally moving table is moved within the furnace from the furnace body transferring truck by suspending up the solidified residual iron;

[0057]FIG. 24 is a cross sectional view showing a structure of the solidified residual iron receiving table provided in the horizontally moving table;

[0058]FIG. 25 is a front elevational view showing a state in which the upper furnace body is descended by the liftjack and the solidified residual iron supported via the suspending band is mounted on the solidified residual iron receiving table;

[0059]FIG. 26 is a front elevational view showing a state in which the solidified residual iron is mounted on the solidified residual iron receiving table and the furnace inner rail is placed on the furnace bottom brick;

[0060]FIG. 27 is a front elevational view showing a state in which the upper furnace body is ascended by the lift jack and the solidified residual iron is suspended up from the solidified residual iron receiving table by using the suspending device and the suspending band;

[0061]FIG. 28 is a perspective view showing a mechanism of making the slide shoe wait by the cylinder for moving along the groove type furnace inner rail;

[0062]FIG. 29 is a front elevational view showing a mechanism of moving the slide shoe by the cylinder for moving along the groove type furnace inner rail;

[0063]FIG. 30 is a side elevational view showing a state in which the slide shoe provided in a lower portion of the horizontally moving table is arranged in correspondence to the groove type furnace inner rail;

[0064]FIG. 31 is an enlarged side elevational view of a portion A in FIG. 30;

[0065]FIG. 32 is a plan view showing a state of using a Y-shaped suspending band;

[0066]FIG. 33 is a plan view showing a state of crossing two band-like suspending bands so as to form an X shape;

[0067]FIGS. 34A and 34B are cross sectional views showing an embodiment of another structure of the solidified residual iron receiving table provided in the horizontally moving table, in which FIG. 34A is a cross sectional view showing a state in which the solidified residual iron is not mounted and FIG. 34B is a cross sectional view showing a state in which a spacer is taken out and the solidified residual iron is mounted.

DESCRIPTION OF THE INVENTION

[0068] A description will be given of a method of scrapping a furnace bottom section of a blast furnace in accordance with the present invention in correspondence to steps thereof.

[0069] As shown in FIG. 1, the structure is made such that a blast furnace 10 is covered with a shell outer side, a stave for cooling is attached to an inner side of the shell, and a brick layer constituted by a fire brick or the like is provided in an inner side of the stave. A connecting portion of the shell is adhered by a welding. A supporting column 15 for being used in a revamping or the like is assembled in an outer side of the blast furnace 10, and a plurality of lift jacks 16 corresponding to an embodiment of vertically moving means are placed in an upper portion of the supporting column 15. The lift jack 16 is employed in the case of assembling the shells divided into a plurality of portions (for example, four) in a vertical direction within the supporting column 15 at a time of installing a new furnace body. In accordance with the present invention, the lift jack 16 is utilized for a scrapping operation of a furnace bottom section 11.

[0070] A furnace bottom brick (normally using a carbon brick) 17 exists in a lowermost portion of the furnace bottom section 11 of the blown out blast furnace 10, a solidified residual iron 19 in which a slug and a coke are mixed and solidified to a pig iron exists on the furnace bottom brick 17, and a collapsible solidified material 18 in which a mixture of the coke, the slug and the like is melted and solidified exists thereon. In order to revamping the furnace bottom brick 17, it is necessary to remove the collapsible solidified material 18 and the solidified residual iron 19. In this case, in the present embodiment, a description will be given of a case of crushing the collapsible solidified material 18 so as to remove by using a construction machinery such as a bulldozer or the like and thereafter suspending up the solidified residual iron 19 so as to remove from the furnace bottom section 11.

[0071] When scrapping the furnace bottom section 11 of the blown out blast furnace 10, at first, a front end portion of a rod 20 suspended from a lift jack 16 placed in the supporting column 15 in such a manner as to freely move vertically is fixed to a top section 14 so as to support the blast furnace 10. Next, the shell of the furnace bottom section 11 is horizontally cut and the shell of the lower furnace body 2 and the lining brick disposed below a cutting position A are taken out. A cutting height is set to be at least higher than the solidified residual iron 19 left in the furnace bottom section 11. When the shell of the lower furnace body 2 of the blast furnace 10 is taken out, the upper furnace body 1 disposed above the cutting position A of the shell is suspended by the lift jack 16 placed in the supporting column 15.

[0072] As shown in FIG. 2, the brick existing within the blast furnace 10 released by taking out the shell in the lower portion is crushed and removed by a construction machinery (not shown). Among furnace inner residues on the furnace bottom brick 17, the collapsible solidified material 18 such as the coke, the slug and the like which can be easily collapsed is conveyed out of the furnace by the construction machinery. Among the furnace inner residues, the solidified residual iron 19 which is hard to be crushed has a weight of 300 to 500 tons. In the blast furnace 10 having a long service life, an erosion area of the furnace bottom brick 17 expands to a lower portion from an outlet port, and a part of the solidified residual iron 19 left in the erosion area is cooled during an operation of the blast furnace so as to be solidified and exists in a state of replacing the furnace bottom brick 17.

[0073] Accordingly, a diameter of the solidified residual iron 19 is substantially close to a diameter of a furnace floor, and in a blast furnace in a class of 5000 m³, it is necessary to convey out a large-size lump having a volume of 250 m³ and a weight of 1300 tons. The solidified residual iron 19 is hard to be crushed by the construction machinery, and there is no way except breaking by a blasting with using a dynamite, however, a long time is required for the blasting operation as mentioned above.

[0074] As shown in FIG. 3, the solidified residual iron 19 exists on the furnace bottom brick 17. The collapsible solidified material 18 is removed, thereafter as shown in FIG. 4, a plurality of cavities 21 are provided at a plurality of portions in the periphery of the solidified residual iron 19 from a surface of the furnace bottom brick 17, and a lifting-up jack 22 is placed in a gap between the solidified residual iron 19 and the furnace bottom brick 17 in a portion of the cavity 21. The cavity 21 can be easily excavated, for example, by a shovel car or the like. Next, as shown in FIG. 5, the solidified residual iron 19 is jacked up in a direction of an arrow by the lifting-up jack 22. An excavating operation of the cavity 21 and a jacking-up operation of the solidified residual iron 19 by the lifting-up jack 22 mentioned above can be performed at a temperature of about 300° C. without cooling a temperature of the solidified residual iron 19 to a room temperature. Accordingly, it is possible to early start a removing operation of the solidified residual iron 19 after blowing out the blast furnace 10.

[0075] Next, as shown in FIGS. 6A and 6B, a suspending device 24 is inserted and fixed to a tuyere 23 arranged in a lower portion of the suspended upper furnace body 1. On the contrary, a suspending band 25 (for example, having a width of 1200 mm and a thickness of about 25 to 50 mm) made of a steel sheet is inserted and extended to a gap between the solidified residual iron 19 and the furnace bottom brick 17 in a direction shown by an arrow. As shown in FIG. 7, after the upper furnace body 1 of the suspended blast furnace 10 is descended by the lift jack 16, the suspending band 25 is connected to the suspending device 24. Next, as shown in FIG. 8, the upper furnace body 1 is ascended by the lift jack 16, the solidified residual iron 19 is suspended by using the suspending device 24 and the suspending band 25, and the operating space is formed between the solidified residual iron 19 and the furnace bottom brick 17.

[0076] An operator 56 places a furnace inner rail 28 used for traveling a horizontally moving table 29 on a surface of the furnace bottom brick 17 as shown in FIG. 11 after forming a surface layer portion of the furnace bottom brick 17 in a flat surface with no unevenness as shown in FIGS. 9 and 10, under this operating space. Otherwise, the furnace bottom brick 17 is removed and the furnace inner rail 28 may be placed on a bottom plate of the blast furnace. As shown in FIG. 12, the horizontally moving table 29 can be easily taken onto the furnace inner rail 28 by using a winch or the like. It is preferable that the horizontally moving table 29 uses a truck provided with a moving roller 30 and a guide roller 31 in a lower portion thereof for being easily moved, for example, as shown in FIGS. 13 to 15. A pair of supporting frames 37 are provided downward on a lower surface of the horizontally moving table 29, a multiplicity of moving rollers 30 connected by an endless chain 38 are provided between these supporting frames 37, and a roller structure body 39 having a guide roller 31 arranged is provided in an outer surface side of the supporting frames 37. The roller structure body 39 employs a roller structure body on the market, is mounted in the lower portion of the horizontally moving table 29 at an interval (for example, in four lines), and is structured such as to move along the groove type furnace inner rail 28.

[0077] In this case, since the furnace inner rail 28 is placed in the furnace bottom brick 17 in which the surface layer portion is formed in a flat surface, or is placed on the bottom plate of the blast furnace by removing all of the furnace bottom brick 17, it is possible to receive a great weight. When a recess portion is partly provided in the furnace bottom brick 17, no problem is generated by charging the recess portion with a mortar so as to form a flat surface and placing the furnace inner rail 28.

[0078] Further, the horizontally moving table 29 may be set to a slide truck, as shown in FIG. 16, structured such that the slide shoe 40 is arranged in the lower portion thereof and the slide shoe 40 is slid along the groove type furnace inner rail 28. A Teflon 41 is adhered to a lower surface of the slide shoe 40 and a stainless steel plate 42 is attached to an upper surface of a groove portion in the furnace inner rail 28 so as to make a coefficient of friction small. Otherwise, as shown in FIG. 17, the structure may be made such that an I-type rail 45 is placed on a flat plate 43 provided on the furnace bottom brick 17 via a level adjusting liner 44 and a truck having wheels is moved thereon, or the structure may be made such that a slide truck is placed on the I-type rail 45 and is slid by employing a lubricating oil, a cleaning material, a soap or the like. In this case, it is important to structure a moving structure for the horizontally moving table 29 which can reduce a coefficient of friction at a low cost and has an improved operability.

[0079] Next, as shown in FIG. 18, the upper furnace body 1 of the blast furnace 10 is descended by the lift jack 16, and the solidified residual iron 19 supported via the suspending device 24 and the suspending band 25 is mounted on the horizontally moving table 29. After separating the suspending device 24 from the tuyere 23, the upper furnace body 1 of the blast furnace 10 is suspended by the lift jack 16 so as to be evacuated upward, as shown in FIG. 19. The suspending device 24 and the suspending band 25 used for suspending up the solidified residual iron 19 are kept being mounted on the horizontally moving table 29 together with the solidified residual iron 19. A rack rail 32 is placed on a moving truck 29 b so as to be connected to the furnace inner rail 28, and the horizontally moving table 29 mounting the solidified residual iron 19 thereon can move toward a furnace body transferring truck 34 provided with a accumulating level adjusting structure 33 and a leveling block 46.

[0080] As shown in FIGS. 19 and 20, the solidified residual iron 19 is taken out from the inner furnace to the outer furnace by moving the horizontally moving table 29 mounting the solidified residual iron 19 thereon onto the rack rail 32 from the furnace inner rail 28 while changing a fixing position of the cylinder for moving 35 arranged near the rack rail 32 forward at every one stroke operation. An embodiment of a mechanism for moving the horizontally moving table 29 by using the cylinder for moving 35 will be shown in FIGS. 28 and 29. A method of operating the mechanism will be later described in detail in combination with a description of FIGS. 28 and 29.

[0081] Next, the moving truck 29 b is moved onto the furnace body transferring truck 34 by operating the cylinder for moving 36 arranged on the furnace body transferring truck 34, as shown in FIG. 21. In the manner mentioned above, the solidified residual iron 19 is mounted on the accumulating level adjusting structure 33 of the furnace body transferring truck 34 together with the horizontally moving table 29 on the rack rail 32 placed on the moving truck 29 b. Subsequently the furnace body transferring truck 34 is moved to a solidified residual iron storage space and a series of scrapping operation of the furnace bottom section of the blast furnace is finished.

[0082] In this case, in accordance with the present invention, it is possible to use the horizontally moving table 29 having a solidified residual iron receiving table 47 as shown in FIG. 22. That is, the horizontally moving table 29 holds the furnace inner rail 28 to the lower portion thereof by a bolt or the like when waiting near the furnace bottom portion 11. Further, as shown in FIG. 23, the horizontally moving table 29 moves onto the furnace bottom brick 17 together with the furnace inner rail 28 in a state of suspending up the solidified residual iron 19. At this time, the horizontally moving table 29 easily moves onto the furnace bottom brick 17 from the furnace body transferring truck 34 by a roller or the like attached to the lower surface of the furnace inner rail 28.

[0083] A plurality of (for example, four) through holes 49 extending in a vertical direction are provided in the solidified residual iron receiving portion 48 on the horizontally moving table 29, and a solidified residual iron receiving table 47 (having a height of about 2.8 m) is detachably arranged in each of the through holes 49. Further, a receiving shelf 50 is arranged at a position corresponding to a middle portion in a height direction of the support of the solidified residual iron receiving table 47 within the through hole 49, as shown in FIG. 24. The solidified residual iron receiving table 47 is supported by a bracket 52 provided on a side surface thereof via a plurality of springs 51 arranged on the receiving shelf 50. When the horizontally moving table 29 waits near the furnace bottom section 11, that is, when the solidified residual iron 19 is not mounted on the solidified residual iron receiving table 47, the lower end surface of the solidified residual iron receiving table 47 moves apart from the furnace bottom brick 17 due to an elastic force of the spring 51, so that it is possible to move the horizontally moving table 29 onto the furnace bottom brick 17 from the outer portion of the furnace.

[0084] Prior to moving the horizontally moving table 29 onto the furnace bottom brick 17, the operating space is formed between the solidified residual iron 19 and the furnace bottom brick 17 as mentioned above, and the operator 56 forms the surface layer portion of the furnace bottom brick 17 in a flat shape under the operating space. After moving the horizontally moving table 29 onto the furnace bottom brick 17, the upper furnace body 1 is descended by the lift jack 16 and the supported solidified residual iron 19 is mounted on the receiving table 47 by using the suspending device 24 and the suspending band 25, as shown in FIG. 25. The spring 51 is compressed via the bracket 52 due to a deadweight of the solidified residual iron 19, and the lower end surface of the solidified residual iron receiving table 47 is grounded on the furnace bottom brick 17. Accordingly, a construction space is formed between the horizontally moving table 29 and the furnace bottom brick 17. As shown in FIG. 26, the operator 56 applies a placing construction of the furnace inner rail 28 on the furnace bottom brick 17 under the construction space, that is, applies a placing construction constituted by charging the lower side of the furnace inner rail 28 with a grout material and aligning a level of the furnace inner rail 28 so as to fix.

[0085] Otherwise, all of the furnace bottom bricks 17 are removed and the furnace inner rail 28 may be placed in the bottom plate of the blast furnace.

[0086] The furnace inner rail 28 is connected to the rack rail 32 placed on the furnace body transferring truck 34 via a furnace outer rail 53.

[0087] Next, as shown in FIG. 27, the upper furnace body 1 is suspended up by the lift jack 16 and the solidified residual iron 19 is evacuated upward from the solidified residual iron receiving table 47. In this case, since the solidified residual iron receiving table 47 is not required, the solidified residual iron receiving table 47 is taken out from the through hole 49. In the case that it is hard to take out within the furnace, the horizontally moving table 29 is taken out onto the rack rail 32 placed in the furnace body transferring truck 34 by using the cylinder for moving 35 so as to be taken out.

[0088] Otherwise, as shown in FIG. 34A, the spacer 54 can be arranged and used on the upper surface of the solidified residual iron receiving table 47. That is, at a time of performing the placing construction of the furnace inner rail 28, the solidified residual iron 19 is mounted on the spacer 54. The lower end surface of the solidified residual iron receiving table 47 is grounded on the furnace bottom brick 17 due to a deadweight of the solidified residual iron 19. Accordingly, the construction space is formed between the horizontally moving table 29 and the furnace bottom brick 17.

[0089] After the placing construction of the furnace inner rail 28 is finished, the solidified residual iron 19 is evacuated upward, the spacer 54 is taken out and the solidified residual iron 19 is again mounted on the solidified residual iron receiving table 47. At this time, the solidified residual iron receiving table 47 descends due to a deadweight of the solidified residual iron 19, however, the lower end surface of the solidified residual iron receiving table 47 is not grounded on the furnace bottom brick 17 and is in an apart state. Accordingly, it is possible to take out the horizontally moving table 29 onto the rack rail 32 placed in the furnace body transferring truck 34 in a state of mounting the solidified residual iron 19 on the solidified residual iron receiving table 47 without taking out the solidified residual iron receiving table 47.

[0090] The cylinder for moving 35 is, for example, horizontally arranged within the groove type furnace inner rail 28 in such a manner as to freely move in a longitudinal direction, as shown in FIGS. 28 and 29. Stopper notches 64 are provided on both side walls of the furnace inner rail 28 at a uniform interval so as to oppose to each other. Further, a first stopper cylinder 57 is horizontally arranged on an upper surface of a cylinder side metal member 56 for holding the cylinder for moving 35 so as to be vertical to the longitudinal direction of the furnace inner rail 28, and a second stopper cylinder 60 is horizontally arranged on a rod side metal member 59 connecting via a piston rod 58 of a cylinder for moving 55 so as to be vertical to the longitudinal direction of the furnace inner rail 28. Further, a plurality of slide shoes 40 arranged in the lower portion of the horizontally moving table 29 via a connection pin 62 are connected to the rod side metal member 59.

[0091] Here, a description will be given of a method of moving the horizontally moving table 29. At first, the first stopper cylinder 57 is extended, and a stopper 61 connected to the first stopper cylinder 57 is protruded to both sides and engaged with the stopper notches 64 provided on both side walls 65 of the furnace inner rail 28. At this time, a stopper 66 connected to the second stopper cylinder 60 is in a state of being retracted. The cylinder for moving 35 in a state of being extended is compressed, the rod 58 is moved to a compression side, and the rod metal member 59 and a plurality of slide shoes 40 are moved along the furnace inner rail 28. Accordingly, the horizontally moving table 29 on which the solidified residual iron receiving table 47 is arranged is moved in a direction of the outer portion of the furnace at a distance of one stroke of the cylinder for moving 35.

[0092] Next, the second stopper cylinder 60 is extended, and a stopper 66 connected to the second stopper cylinder 60 is protruded to both sides and engaged with the stopper notches 64 provided on both side walls 65 of the furnace inner rail 28. On the contrary, the first stopper cylinder 57 is compressed, and the stopper 61 connected to the first stopper cylinder 57 is made in a retracted state so as to be taken out from the stopper notches 64 provided on both side walls 65 of the furnace inner rail 28. The cylinder for moving 35 in a compressed state is extended and the cylinder side metal member 56 is moved in a direction of the outer portion of the furnace at a distance of one stroke.

[0093] Subsequently, the first stopper cylinder 57 is extended, and the stopper 61 connected to the first stopper cylinder 57 is protruded to both sides and engaged with the stopper notches 64 provided on both side walls 65 of the furnace inner rail 28. On the contrary, the second stopper cylinder 60 is compressed, the stopper 66 connected to the second stopper cylinder 60 is retracted to both sides so as to be taken out from the stopper notches 64 provided on both side walls 65 of the furnace inner rail 28, and the cylinder for moving 35 is compressed. The horizontally moving table 29 on which the solidified residual iron receiving table 47 is arranged is moved in a direction of the outer portion of the furnace by repeating the operations mentioned above.

[0094] In this case, a description is given of the method of moving the horizontally moving table 29 by using the cylinder for moving 35, however, it is possible to move the horizontally moving table 29 in the same manner by using a center hole jack or the like.

[0095] Further, as shown in FIG. 30, for example, four lines of slide shoes 40 are arranged in the lower portion of the horizontally moving table 29, and the slide shoes 40 slide along the groove type furnace inner rail 28 placed on the furnace bottom brick 17. As shown in FIG. 31, it is preferable to make the structure such that the Teflon 41 is adhered to the lower surface of the slide shoe 40 and the stainless steel plate 42 is attached to the inner surface of the furnace inner rail 28 so as to make a coefficient of friction small.

[0096] Further, in accordance with the present invention, it is preferable to make the structure such that the suspending band 25 integrally formed in a Y shape shown in FIG. 32 is used. That is, one of rectangular bands 25 a radially extending in three directions of the Y-shaped suspending band 25 is moved in a direction shown by an arrow in a state of being directed to a center of the blast furnace 10. A position at which the lifting-up jack 22 for jacking up the solidified residual iron 19 is placed is selected to a position at which the Y-shaped suspending band 25 is not interfered at a time of being moved. It is possible to stably suspend up the solidified residual iron 19 by using the Y-shaped suspending band 25 in the manner mentioned above.

[0097] An angle of the rectangular band 25 a radially extending in three directions of the Y-shaped suspending band 25 is not always required to be set to 120 degrees. When setting an angle α formed by two rectangular bands 25 a positioned at the rear portion to 120 degrees or less (for example, about 90 degrees) in a state of moving the Y-shaped suspending band 25 toward the center of the blast furnace 10, an area for placing the lifting-up jack 22 is expanded, so that it is possible to stably jack up the solidified residual iron 19.

[0098] In the case of using web-shaped suspending band 25 b in place of the Y-shaped suspending band 25, it is preferable to structure such that two web-shaped suspending bands 25 b are used by being crossed so as to form an X shape, as shown in FIG. 33. An angle formed by two web-shaped suspending bands 25 b being crossed in the X shape is not particularly limited. However, when the lifting-up jack 22 is placed in an area having a larger angle among the angles formed by two web-shaped suspending bands 25 b, it is possible to stably jack up the solidified residual iron 19.

[0099] As described above, in accordance with the present invention, since the solidified residual iron 19 is vertically moved by the lift jack 16 placed in the supporting column 15 for supporting the blast furnace 10, it is not necessary to newly provide vertically moving means for the solidified residual iron 19. Further, since the solidified residual iron 19 is suspended up by connecting the suspending band 25 to the shell side suspending device 24 fixed to the lower end portion of the upper furnace body 1, it is possible to move the large lump of solidified residual iron 19 without separating. Further, since the operation can be performed in a state of high temperature, it is possible to reduce a time required for scrapping the furnace bottom section 11.

[0100] However, in the case that the weight of the solidified residual iron 19 is too heavy to be within an allowable range of the suspending band 25 and the vertically moving means, the solidified residual iron 19 may be suspended up in accordance with the method mentioned above after being divided. Further, in the case that the size of the solidified residual iron 19 is too large to be conveyed, the solidified residual iron 19 may be divided on the horizontally moving table 29 after being mounted on the horizontally moving table 29.

[0101] Further, in order to stably suspend up the solidified residual iron 19, the solidified residual iron 19 may be suspended up by arranging a beam within the upper furnace body, connecting the beam to the solidified residual iron 19 by employing the suspending-up member and using the suspending-up member and the supporting band 25 or piercing three or more holes in the solidified residual iron 19 so as to extend through the suspending rod. 

1. A method of scrapping a furnace bottom section of a blast furnace comprising the steps of: horizontally cutting a furnace body of the blast furnace after being blown out at a position higher than a solidified residual iron left in the furnace bottom section; suspending an upper furnace body above the cutting position by employing vertically moving means placed in a supporting column; taking out at least a part of a shell and a lining brick in a lower furnace body below said cutting position all around the periphery; and thereafter conveying said solidified residual iron out of the furnace, wherein said upper furnace body and said solidified residual iron are integrally connected by using a suspending device before conveying said solidified residual iron out of the furnace, and said upper furnace body and said solidified residual iron are vertically moved by using said vertically moving means.
 2. A method of scrapping a furnace bottom section of a blast furnace according to claim 1, wherein a plurality of cavities are provided along a peripheral portion of said solidified residual iron and at a plurality of portions between said solidified residual iron and the furnace bottom brick before conveying said solidified residual iron out of the furnace, said solidified residual iron is jacked up by a lifting-up jack arranged in said cavity so as to form a gap between said solidified residual iron and said furnace bottom brick, a solidified residual iron suspending band is inserted into said gap, thereafter said upper furnace body suspended in said supporting column is descended by using said vertically moving means so that said solidified residual iron suspending band is connected to said suspending device fixed to a lower portion of said upper furnace body, next said upper furnace body is suspended up together with said solidified residual iron by using said vertically moving means so that an operating space is formed between said solidified residual iron and said furnace bottom brick or a bottom plate of the blast furnace, a horizontally moving table is moved on said furnace bottom brick or said bottom plate of the blast furnace, thereafter said upper furnace body and said solidified residual iron are descended by using said vertically moving means so as to be mounted on said horizontally moving table, next said suspending device fixed to the lower portion of said upper furnace body is separated, thereafter said upper furnace body is evacuated upward by using said vertically moving apparatus, and said horizontally moving table mounting said solidified residual iron thereon is moved from the inner portion of the furnace to the outer portion of the furnace.
 3. A method of scrapping a furnace bottom section of a blast furnace according to claim 2, wherein said suspending device is fixed to a tuyere of said upper furnace body.
 4. A method of scrapping a furnace bottom section of a blast furnace according to claim 2 or 3, wherein a surface layer portion of said furnace bottom brick is flattened under said operating space formed between said solidified residual iron and said furnace bottom brick, or said furnace bottom brick is removed, thereafter a furnace inner rail is placed on said furnace bottom brick or said bottom plate of the blast furnace, and said horizontally moving table is moved on said furnace inner rail.
 5. A method of scrapping a furnace bottom section of a blast furnace according to claim 2 or 3, wherein a surface layer portion of said furnace bottom brick is flattened under said operating space formed between said solidified residual iron and said furnace bottom brick, or said furnace bottom brick is removed, thereafter said horizontally moving table having a solidified residual iron receiving table detachably arranged in a plurality of through holes is moved onto said furnace brick or said bottom plate of the blast furnace, said upper furnace body and said solidified residual iron are descended by using said vertically moving means so as to be mounted on said solidified residual iron receiving table, a lower end surface of said solidified residual iron receiving table is grounded on said furnace bottom brick or said bottom plate of the blast furnace due to a deadweight of said solidified residual iron so that a construction space is formed between said horizontally moving table and said furnace bottom brick or said bottom plate of the blast furnace, the furnace inner rail is placed on said furnace bottom brick or said bottom plate of the blast furnace under said construction space, thereafter said upper furnace body and said solidified residual iron are suspended up by using said vertically moving means so that said solidified residual iron receiving table is taken out from said horizontally moving table, said upper furnace body and said solidified residual iron are descended by using said vertically moving means so as to be mounted on said horizontally moving table, next said suspending device fixed to the lower end portion of said upper furnace body is removed, thereafter said upper furnace body is evacuated upward by using said vertically moving apparatus, and said horizontally moving table mounting said solidified residual iron thereon is moved to the outer portion of the furnace from the inner portion of the furnace.
 6. A method of scrapping a furnace bottom section of a blast furnace according to claim 5, wherein a receiving shelf is provided in said through hole provided in said horizontally moving table, said solidified residual iron receiving table is supported to said receiving shelf via a plurality of springs by a bracket provided on an upper side surface thereof, a lower end surface of said solidified residual iron receiving table is moved apart from said furnace bottom brick or said bottom plate of the blast furnace due to an elastic force of said spring when said horizontally moving table is moved onto said furnace bottom brick or said bottom plate of the blast furnace, said spring is compressed via said bracket when said solidified residual iron is mounted on said solidified residual iron receiving table so that the lower end surface of said solidified residual iron receiving table is grounded on said furnace bottom brick or said bottom plate of the blast furnace, and said construction space is formed between said horizontally moving table and said furnace bottom brick or said bottom plate of the blast furnace.
 7. A method of scrapping a furnace bottom section of a blast furnace according to claim 2, 3, 4, 5 or 6, wherein said horizontally moving table arranged on said furnace inner rail is moved via a roller or a slide shoe arranged in a lower portion of said horizontally moving table.
 8. A method of scrapping a furnace bottom section of a blast furnace according to claim 7, wherein said slide shoe is arranged within a groove formed in said furnace inner rail, a friction coefficient reducing member is interposed between said slide shoe and the groove formed in said furnace inner rail, and said horizontally moving table is moved due to a slide motion along the groove formed in said furnace inner rail of said slide shoe.
 9. A method of scrapping a furnace bottom section of a blast furnace according to claim 8, wherein said friction coefficient reducing member is made of a Teflon and/or a stainless steel.
 10. A method of scrapping a furnace bottom section of a blast furnace according to claim 2, 3, 4, 5, 6, 7, 8 or 9, wherein a shape of said solidified residual iron suspending band is formed in a Y shape.
 11. A method of scrapping a furnace bottom section of a blast furnace according to claim 2, 3, 4, 5, 6, 7, 8 or 9, wherein a shape of said solidified residual iron suspending band is formed in a web shape, and said solidified residual iron is suspended up by crossing said two web-like solidified residual iron suspending bands so as to form an X shape.
 12. A method of scrapping a furnace bottom section of a blast furnace according to claim 2, 3, 4, 5, 6, 7, 8, 9, 10 or 11, wherein said solidified residual iron is separated so as to be suspended up together with said upper furnace body by using said vertically moving means.
 13. A method of scrapping a furnace bottom section of a blast furnace according to claim 2, 3, 4, 5, 6, 7, 8, 9, 10, 11 or 12, wherein said solidified residual iron mounted on said horizontally moving table is separated.
 14. A method of scrapping a furnace bottom section of a blast furnace according to claim 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12 or 13, wherein a beam is arranged within said upper furnace body, said beam and said solidified residual iron are connected by using the suspending-up member, and said solidified residual iron is suspended up by using said suspending-up member and said solidified residual iron suspending band. 